Introduction
  Description


MSVLA series is the military grade cable and wire identificationsleeves, which is made of cross-linked environmentally friendly polyolefinbombarded by high-power electron beam with electronic accelerators to meetrequirements of high end markets where highly reliable cable& wireidentification is required. It accords to Classes 1 and 3 of AMS-DTL-23053/5half-hard high molecular materials. For this product, both 2:1 and 3:1 shrinkratio are available on your request. 


Features


  • Military grade, lightweight, well suited for aerospace vehicles, tank, and submarines identification purposes
  • High temperature resistant(temperature rating 135°C/275°F)
  • Highly flame retardant, VW-1
  • RoHS compliant
  • Highly reliable and permanent identification
  • Thermo-sensitive, quick recovery
  • Computer-printable, any characters and logo are easy to design
Rated Temperature

Continuous operating temperature: -55°C~135°C/-67°F~275°F
Min. shrink temperature: 85°C/185°F
Full recovery temperature: 115°C~200°C/239°F~392°F, 8~3minutes
Max. storage and transportation temperature: ≤+50°C/122°F


Standards
  • Meets AMS-DTL-23053/5, compatibility: UL224
  • Color code soundness: SAE-AS 81531 and MIL-STD-202F/215J


 Dimension(2:1)
Order Description Expanded As Supplied(mm) Recovered After Heating(mm)
Inner Diameter ID1 Flatten width G Dual Wall Thickness H Inner DiameterID2 Single Wall Thickness h
MSVLA-2X-1.6/ 2.00±0.20 3.7±0.3 0.48±0.10 ≤0.79 0.45±0.06
MSVLA-2X-2.4/ 2.79±0.20 5.0±0.3 0.48±0.10 ≤1.18 0.49±0.06
MSVLA-2X-3.2/ 3.64±0.23 6.3±0.4 0.48±0.10 ≤1.59 0.51±0.06
MSVLA-2X-4.8/ 5.26±0.25 8.9±0.4 0.49±0.10 ≤2.36 0.54±0.06
MSVLA-2X-6.4/ 6.92±0.28 11.5±0.4 0.50±0.10 ≤3.18 0.56±0.06
MSVLA-2X-9.5/ 10.2±0.32 16.7±0.5 0.51±0.11 ≤4.75 0.59±0.06
MSVLA-2X-12.7/ 13.5±0.36 21.8±0.6 0.52±0.11 ≤6.35 0.60±0.07
MSVLA-2X-19/ 20.1±0.40 32.2±0.6 0.53±0.11 ≤9.53 0.62±0.07
MSVLA-2X-25/ 26.7±0.45 42.5±0.7 0.55±0.12 ≤12.7 0.63±0.07
MSVLA-2X-38/ 39.8±0.51 63.2±0.8 0.57±0.12 ≤19.1 0.64±0.07
MSVLA-2X-51/ 53.0±0.56 83.9±0.9 0.58±0.13 ≤25.4 0.64±0.08
MSVLA-2X-76/ 79.4±0.56 125.3±1.0 0.59±0.13 ≤38.1 0.64±0.09
 


Dimension(3:1)
Order Description Expanded As Supplied(mm) Recovered After Heating(mm)
Internal Diameter ID1 Flatten Width G Dual Wall Thickness H Inner Diameter ID2 Single Wall Thickness
MSVLA-3X-1.6/ 2.00±0.20 3.7±0.3 0.47±0.10 ≤0.53 0.52±0.06
MSVLA-3X-2.4/ 2.79±0.20 5.0±0.3 0.47±0.10 ≤0.79 0.57±0.06
MSVLA-3X-3.2/ 3.64±0.23 6.3±0.4 0.48±0.10 ≤1.06 0.61±0.06
MSVLA-3X-4.8/ 5.26±0.25 8.9±0.4 0.49±0.10 ≤1.59 0.67±0.06
MSVLA-3X-6.4/ 6.92±0.28 11.5±0.4 0.50±0.10 ≤2.36 0.71±0.06
MSVLA-3X-9.5/ 10.2±0.32 16.7±0.5 0.52±0.11 ≤3.18 0.77±0.06
MSVLA-3X-12.7/ 13.5±0.36 21.8±0.6 0.53±0.11 ≤4.75 0.80±0.07
MSVLA-3X-19/ 20.1±0.40 32.2±0.6 0.55±0.11 ≤6.35 0.84±0.07
MSVLA-3X-25/ 26.7±0.45 42.5±0.7 0.56±0.12 ≤8.47 0.86±0.07
MSVLA-3X-38/ 39.8±0.51 63.2±0.8 0.57±0.12 ≤12.9 0.89±0.07
MSVLA-3X-51/ 53.0±0.56 83.9±0.9 0.57±0.13 ≤17.2 0.90±0.08
MSVLA-3X-76/ 79.4±0.56 125.3±1.0 0.59±0.13 ≤25.8 0.92±0.09
 
 
Standard Packaging Data:
No. Sizes Packaging(Pcs/Reel)
Box 210 Box 146
1 Φ1.6 2500 250
2 Φ2.4 2500 250
3 Φ3.2 2000 250
4 Φ4.8 2000 250
5 Φ6.4 1500 250
6 Φ9.5 1000 250
7 Φ12.7 500 250
8 Φ19 500 250
9 Φ25 500 250
10 Φ38 250 250
11 Φ51 250 250
12 Φ76 250 250
 
 
Physicochemical& Electrical Performance
Performance Indicators Test Method
 Typical properties Unit States
Tensile Strength Mpa Unaged ≥10.3 ASTM G 154,MIL-DTL-23053E
ISO 37,500mm/min
175°C,168h,ISO 188
Heat aged/ After fluids/UV aged ≥6.9
Elongation at break % Unaged ≥200
Heat aged/ After fluid ≥100
Secant Modulus Mpa Unaged <173 ASTM D 882
Voltage Withstand V Unaged / After aged 2500V, No breakdown in 60 sec. IEC 243,ASTM G 154
175°C,168h,ISO 188
Dielectric Strength MV/m Before aged ≥19.7
Heat aged/ After fluid/ UV aged ≥15.8
Volume Resistivity Ω.cm Unaged ≥1014 IEC 93
Dielectric constant - Unaged ≤3.1 ASTM 150
Water Absorption - Unaged ≤0.5% ASTM 570,23°C,24h
Bare Copper Corrosion - Unaged No corrosion 23°C,Rh 95±5%,24h
175°C,16h
Heat Shock - Unaged No cracks, flowing, dripping Wind to the specified mandrel,225°C,4h
Cold Flexibility - Unaged No cracks Wind to the specified mandrel,-30°C,1h
Flammability - Unaged VW-1 IEC 60332-1-3 Ed.1.0 b:2004
Longitudinal Change % Unaged 2X:-10~+1 200°C,Constant 3min
3X:-15~+5
Smoke Density - Unaged - DIN 5510-2
Toxcity Index - Unaged - BS 6853:1999
 